(d) measured current by the Rogowski coil at 14 kV
Figure 8: Microstructure and EDA line scan of weld interface based on MP and SP coil at
9.8 kJ: (a) and (b): 5754 (1.0 mm)/DP600, (c) and (d): 1060 (1 [...] coil allows for a variety of
experiments. From the Fig. 8(e), it is evident that high-quality joints can be achieved at
higher energy levels. At 8.45 kJ, the 1060 (1.0 mm) / DP450 joint and the 5754 (0 [...] successful welding of 1060 (1.0 mm) / DP450 (1.0 mm) at 6.05 kJ and 5754 (1.0 mm) /
DP600 (1.0 mm) at 9.8 kJ, with all interfaces displaying metallurgical characteristics. These
findings confirm the excellent …